NICKEL PLATING PROCESSES
BRIGHT NICKEL

Process

Operating Conditions

Application
TOPGLOW BRIGHT
NICKEL 622
TOPGLOW BRIGHT
NICKEL SALT 622

TOP GLOW ADDITIVE 623
TOP GLOW BRIGHTNER 624

TOP GLOW WETTER
TEMPERATURE
pH
CATHODE CURRENT DENSITY
375–425g/l


8 – 10 ml/l
0.3–0.6ml/l

2 - 4 ml/l
50 – 60C
4.2 – 4.6
2.0 – 4.0A/dm
A versatile bright nickel system which
produces mirror bright leveled deposits.
Excellent chrome receptivity
Very good low current density brightness.
Suitable both for vat and barrel.
TOPFLOW BRIGHT NICKEL 601TOP FLOW BRIGHT
NICKEL SALT 601

TOP FLOW ADDITIVE 602

TOP FLOW BRIGHTNER 603
TOP FLOW WETTER 604
TEMPERATURE
pH
CATHODE CURRENT DENSITY
375–425g/1


8 – 10 ml/1

0.2–0.4ml
1 – 2ml/l
50 – 60C
4.2 – 4.6
2.0 – 4.0A/dm
An ultra high performance economical bright nickel.
Exceptionally good leveling and brightness.
Low brightener consumption.
MAGNA BRIGHT NICKEL 631MAGNA BRIGHT NICKEL
SALT 631
NICKEL SULPHATE
NICKEL CHLORIDE
BORI ACID MAGNA ADDITIVE 632
MAGNA BRIGHTNER 633
MAGNA WETTER (optional)

TEMPERATURE
pH
CATHODE CURRENT DENSITY
375–425g/l

275–325g/l
50–70g/l
35-45g/l
8–10 ml /l
0.2–0.4ml
0.4–0.6ml
50–60C
4.2–4.6
2.0–4.0A/dm
Designed primarily for depositing highly leveled ductile
deposits over sulphur free semi bright nickel coatings.
Very good coverage even at L.C.D area.
Trouble free bright nickel process.
Maximum brightness over a wide range of operating conditions.
Wide bath chemistry.
SWIFT BRIGHT NICKEL 681SWIFT BRIGHT NICKEL
SALT 681
SWIFT ADDITIVE 682
SWIFT BRIGHTNER 683
SWIFT ANTIPIT 684(optional)
TEMPERATURE
pH
CATHODE CURRENT DENSITY
375–425g/l

8–10 ml/l
0.2–0.4ml/l
0.4–0.6ml/l
50–60C
4.2–4.6
2.0–4.0A/dm
Less deposit thickness for the desired finish.
Fewer rejection due to passive nickel deposits.
Ultimate in leveling.
Production proven process.
NIAGRA BRIGHT NICKEL 613NIAGRA BRIGHT NICKEL
SALT 613
NIAGRA ADDITIVE 614
NIAGRA BRIGHTNER 615
SWIFT ANTIPIT 616(optIONAL)
TEMPERATURE
pH
CATHODE CURRENT DENSITY
375–425g/1

8–10 ml/l
0.2–0.4ml/l
0.4–0.6ml/l
50–60C
4.2–4.6
2.0–4.0A/dm
Ultra high performance bright nickel system.
Versatile brightener system. Gives excellent results in vat nickel formulations.
SMUG LEVELLER 675SMUG LEVELLER 675 0.2–0.4ml/lAn addition agent for bright nickel to impart
additional leveling on poorly polished surface.
PURGATIVE PURIFIER 676PURGATIVE PURIFIER 676 0.4–0.8ml/lA purifier for bright nickel solutions to improve
tolerance to metallic impurities like copper and zinc.
DOUBLE ACTION PURIFIER 678DOUBLE ACTION PURIFIER 678 0.2–0.8ml/lAn exceptional product which give high tolerance
to metallic impurities.
Eliminates frequent time consuming dummying.
Improves the nickel coverage.
BLACK NICKEL
BLACK NICKEL

BLACKAMOOR BLACK NICKEL 694
BLACKAMOOR BLACK
NICKEL SALT 694

TEMPERATURE
pH
Current density
175–225 g/l


40–50C
5.2–5.8
0.1–1.0A/dm
The process produces rich black colored deposit which
has a good decorative appearance
NIGRO BLACK NICKEL 696NIGRO BLACK NICKEL SALT 696

NIGRO ADDITIVE 697
NIGRO ANTIPIT 698
TEMPERATURE
pH
Current density
225–275g/l


175–225g/l
1–3g/l
60–70C
3.5–4.5
2–3A/dm
New advance technology.
Particularly suitable for
components such as camera fittings, optical, electrical instruments, jewellery articles
SATIN NICKEL
SILNIK SATIN NICKEL 627SILNIK SATIN NICKEL
SALT 627
SILNIK ADDITIVE A
SILNIK ADDITIVE B
SILNIK SATINIZER 628
TEMPERATURE
pH
Current density
550 – 600g/l

8 – 12ml/l
8 – 12ml/l
1 – 2ml/
48 – 52C
4.0 – 4.3
4 – 6A/dm
The new supra semi bright process is
based on advanced technology to produce high corrosion resistant deposits.
Production proven process used extensively
in fully automatic installation